highwayman,
Thin sheetmetal is hard to weld and you are doing a great job. My only comment would be to maybe kick up the heat a bit, or the travel speed.
If those beads don't penetrate 100%, when you grind them off, not much will be left. See what the weld looks like from the back..it needs to be well joined with filler metal too.
Stuart
